Pengaruh Fraksi Volume Pada Uji Mekanis Komposit Hybrid Dari Serat Sabut Kelapa Dan Serat Batang Pisang Bermatrix Epoxy
DOI:
https://doi.org/10.55606/teknik.v5i2.7587Keywords:
hybrid composite, volume fraction, coconut coir, banana stem, mechanical properties, epoxyAbstract
Abstract. The increasing demand for eco-friendly and recyclable materials has driven the development of natural fiber-based composite materials. This study aims to analyze the effect of volume fraction variation on the mechanical properties of hybrid composites made from coconut coir fiber and banana stem fiber with an epoxy matrix. The research employed an experimental method with variations of fiber volume fractions at 40%, 30%, and 20%, and mechanical testing including tensile, bending, and impact tests based on ASTM standards. The results showed that the highest tensile strength was achieved by the composite with a 60% matrix and 40% fiber volume fraction, reaching 21.16 MPa. Meanwhile, the highest bending strength and impact resistance were obtained by the composite with an 80% matrix and 20% fiber volume fraction, at 49.46 MPa and 0.00837 Joule/mm², respectively. Increasing the fiber content tends to enhance tensile strength but reduces bending strength and impact resistance due to uneven resin distribution and the formation of voids. This hybrid composite has potential as an environmentally friendly material alternative with competitive mechanical properties.
References
Admin, A., Sehono, S., & Rizki Putra, I. (2022). Analisis kekuatan tarik dan bending komposit serat pelepah pisang. Teknika STTKD: Jurnal Teknik, Elektronik, Engine, 8(1), 167–174.
Angelia, A., Ghofur, M. A., Nugroho, A. D., Purwadi, P., & Herlambang, P. (2020). Analisis kekuatan tarik, bending, mikrostruktur, komposisi dan kemampuan redam suara komposit serat pelepah pisang menggunakan metode Vacuum Assisted Resin Infusion. Prosiding SENATIK ITD Adisutjipto Yogyakarta, 6, 67-80.
Bifel, R. D. N., Maliwemu, E. U., & Adoe, D. G. (2015). Pengaruh Perlakuan Alkali Serat Sabut Kelapa terhadap Kekuatan Tarik Komposit Polyester. Lontar Jurnal Teknik Mesin Undana, 2(1), 61-68.
Dzaky Syamsuri, N., Hartono, P., & Choirotin, I. (2020). Epoxy terhadap sifat mekanik pada komposit. D, 64–69.
Farrel, D. A., Yuliyanto, & Zulfitriyanto. (2022). Pengaruh sifat mekanik komposit serat sabut kelapa bermatrik polyester terhadap pengujian tarik. Jurnal Indonesia Sosial Teknologi, 3(2), 219–230.
Gunandar, A. W. (2021). Analiis Kekuatan Tarik Dan Impak Bahan Komposit Hybrid Berpenguat Serbuk Kayu Akasia dan Tandan Kosong Kelapa Sawit. Tugas Akhir. (Tugas Akhir, Universitas Islam Riau Pekanbaru)
Gundara, G., & Rahman, M. B. N. (2019). Sifat tarik, bending dan impak komposit serat sabut kelapa-polyester dengan variasi fraksi volume. Jurnal Material dan Proses Manufaktur, 3(1), 10-19.
Harita, E. A. (2022). Karakteristik Sifat Mekanik Komposit Serat Bambu Resin Polyester dengan Filler Serabut Kelapa (Doctoral dissertation, Politeknik Manufaktur Negeri Bangka Belitung).
Haryanti, N. H., & Wardhana, H. (2020). Potensi Serat Alam Sebagai Material Komposit. Banjarmasin: Lambung Mangkurat University.
Irawan, A. P., & Sukania, I. W. (2022). Kekuatan tekan komposit serat limbah pisang dengan matriks epoksi sebagai bahan socket prosthesis. Prosiding Konferensi Nasional Engineering Perhotelan VI, 1, 291–295.
Kardiman, D., & Rahmalina, D. (2023). Pengembangan komposit matrik epoxy melalui penambahan penguat serat rami dan fiberglass dengan variasi 2 – 4 wt%. Teknobiz : Jurnal Ilmiah Program Studi Magister Teknik Mesin, 13(2), 80–86.
Kurniawan, N. A., Setiawan, F., & Sofyan, E. (2022). Pengujian tarik komposit spesimen campuran serat pisang alur diagonal dan pasir besi dengan matrik resin polyester dengan metode hand lay-up. Teknika STTKD: Jurnal Teknik, Elektronik, Engine, 8(2), 281–288.
Mahmud, M. Z. A., Chowdhury, M. S., Sarker, M. A. H., Rabbi, S. M., Rayhan, M. T., Reja, R. I., & Mobarak, M. H. A thorough analysis of the tensile, bending, impact, and sem microstructure of jute fabric epoxy reinforced with tiny fibers from banana and coconut (Under Review)
Nisa’, U. (2020). Pembuatan Komposit Material Peredam Akustik Berbahan Dasar Dari Serat Sabut Kelapa, Pelepah Pisang, Lidah Mertua dan Epoxy Resin. (Skripsi Sarjana, UIN Walisongo).
Patandean, T. W., & Usman, A. M. S. (2023). Kaji Eksperimental Sifat Mekanik Komposit Resin Epoxy Berpenguat Serat Alam (Doctoral dissertation, Politeknik Negeri ujung Pandang).
Paundra, F., Muttaqin, Z. Z., Nurullah, F. P., Pujiyulianto, E., & Darsono, F. B. (2022). Pengaruh variasi fraksi volume terhadap kekuatan tarik komposit berpenguat gabungan serat pelepah pisang dan serat daun nanas. Journal of Science, Technology, and Visual Culture, 2(2), 213-217.
Reynaldi, I. Z., Sehono, S., & Putra, I. R. (2022). Analisis kekuatan tarik dan bending dari komposit serat pelepah pisang menggunakan metode hand lay up dengan variasi perbandingan berat. Teknika STTKD: Jurnal Teknik, Elektronik, Engine, 8(1), 152-159.
Safriani, N., Kurniawan, E., Bahri, S., Ishak, I., & Jalaluddin, J. (2021). Pembuatan komposit hybrid dari serbuk bentonit dan pelepah pisang dengan penguat matrik polysterena. Chemical Engineering Journal Storage, 1(2), 35-45.
Salman, S., Fajar, M., & Hazmi, M. (2023). Pengaruh fraksi volume serat sabut kelapa dengan inti serbuk gergaji kayu sengon terhadap kekuatan bending komposit hybrid sandwich. Jurnal Teknologi, 15(1), 167-174.
Subhan, M., Ergiantoro, A., & Yuliyanto, Y. (2023). komposit hybride serat buah kelapa dan tebu pada bagian akar, batang, pucuk bermatrix polyester BQTN 157. Manutech: Jurnal Teknologi Manufaktur, 15(02), 191-197.
Suteja, S., Purnowidodo, A., Darmadi, D. B., & Sari, N. H. (2019). Perilaku tarik komposit laminat serat kulit waru-aluminium. Jurnal Rekayasa Mesin, 10(1), 17-24.
Umar, M. H., & Mujiburrohman, M. (2019). Pengaruh Fraksi Volume Penguat Terhadap Kekuatan Komposit dari Serbuk Sabut Kelapa dan Serat Pelepah Batang Pisang-Epoxy. (Doctoral dissertation, Universitas Muhammadiyah Surakarta).
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2025 Jurnal Teknik Mesin, Elektro dan Ilmu Komputer
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.